Laserfiche WebLink
SPEC <br />2360 <br />MODIFIED LOTTMAN <br />MIX TYPE <br />TREATED SPECIMENS <br />SPWEA340B 11% <br />DATE <br />5/7/2015 <br />UNTREATED SPECIMENS <br />SAMPLE I.D. <br />DIAMETER <br />THICKNESS <br />DRY WT. IN AIR <br />SSD WT. <br />WT. IN H2O <br />VOLUME <br />BULK Sp. Gr. <br />MAX Sp. Gr. <br />% AIR VOIDS <br />VOLUME AIR VOIDS <br />LOAD, POUNDS <br />1 <br />3 <br />2 <br />4 <br />150 <br />150 <br />150 <br />150 <br />95.00 <br />95 <br />95.00 <br />95.00 <br />3587.7 <br />3591.1 <br />3588.7 <br />3592.0 <br />3597.0 <br />3602.0 <br />3600.1 <br />3604.3 <br />1950.9 <br />1958.0 <br />1961.0 <br />1960.2 <br />1646.1 <br />1644.0 <br />1639.1 <br />1644.1 <br />2.180 <br />2.184 <br />2.182 <br />2.189 <br />2.185 <br />2.187 <br />2.451 <br />2.451 <br />2.451 <br />2.451 <br />2.451 <br />2.451 <br />11.1 <br />10.9 <br />11.0 <br />10.7 <br />10.9 <br />10.8 <br />182.33 <br />178.84 <br />180.59 <br />2249 <br />2296 <br />2273 <br />SATURATED FOR <br />MIN. @ <br />SSD WT. <br />3706.4 <br />3707.5 <br />WT. IN H2O <br />2052.2 <br />2051.5 <br />VOLUME <br />1654.2 <br />1656.0 <br />VOL. OF ABS. H2O <br />118.7 <br />116.4 <br />% SATURATION <br />65.1 <br />65.1 <br />65.1 <br />% SWELL <br />0.49 <br />0.73 <br />0.6 <br />DIAMETER <br />THICKNESS <br />SSD WT. <br />WT. IN H2O. <br />VOLUME <br />VOL. OF ABS. H2O <br />% SATERATION <br />% SWELL <br />LOAD IN POUNDS <br />DRY STRENGTH <br />WET STRENGTH <br />TSR <br />% VIS. STRIPPING <br />% BROKEN AGG. <br />mm.Hg <br />BLOWS na <br />CONDITIONED 24 HOURS IN 140 DEGREE F. WATER <br />150.1 <br />94.780 <br />3672.2 <br />2029.5 <br />1642.7 <br />149.95 <br />94.500 <br />3676.8 <br />2029.2 <br />1647.6 <br />84.5 <br />85.7 <br />46.3 <br />47.9 <br />-0.21 <br />0.22 <br />0.01 <br />1529 <br />1529 <br />1529 <br />64.8 <br />66.2 <br />65.5 <br />44.1 <br />44.3 <br />44.2 <br />67.4 <br />67.7 <br />67.5 <br /><10 <br /><10 <br />Tested By: CW <br />Date: 5/8/15 <br /><10 <br /><10 <br />Reviewed By: AH <br />Date: 5/12/15 <br />G-6 <br />