Laserfiche WebLink
SPEC <br />2360 <br />MODIFIED LOTTMAN <br />MIX TYPE <br />TREATED SPECIMENS <br />SPWEA340B 7% <br />DATE <br />4/27/2015 <br />UNTREATED SPECIMENS <br />SAMPLE I. D. <br />DIAMETER <br />THICKNESS <br />DRY WT. IN AIR <br />SSD WT. <br />WT. IN H2O <br />VOLUME <br />BULK Sp. Gr. <br />MAX Sp. Gr. <br />% AIR VOIDS <br />VOLUME AI R VOIDS <br />LOAD, POUNDS <br />1 <br />2 <br />3 <br />4 <br />150 <br />150 <br />150 <br />150 <br />95.00 <br />95 <br />95.00 <br />95.00 <br />3754.6 <br />3751.8 <br />3754.5 <br />3755.9 <br />3763.0 <br />3758.6 <br />3762.7 <br />3764.2 <br />2113.3 <br />2115.0 <br />2112.5 <br />2116.7 <br />1649.7 <br />1643.6 <br />1650.2 <br />1647.5 <br />2.276 <br />2.283 <br />2.279 <br />2.275 <br />2.280 <br />2.277 <br />2.456 <br />2.456 <br />2.456 <br />2.456 <br />2.456 <br />2.456 <br />7.3 <br />7.1 <br />7.2 <br />7.4 <br />7.2 <br />7.3 <br />120.95 <br />115.99 <br />118.47 <br />2710 <br />2733 <br />2722 <br />SATURATED FORI I MIN. @ <br />SSD WT. <br />3833.7 <br />3827.9 <br />WT. IN H2O <br />2177.6 <br />2183.1 <br />VOLUME <br />1656.1 <br />1644.8 <br />VOL. OF ABS. H2O <br />79.1 <br />76.1 <br />% SATURATION <br />65.4 <br />65.6 <br />65.5 <br />% SWELL <br />0.39 <br />0.07 <br />0.2 <br />DIAMETER <br />THICKNESS <br />SSD WT. <br />WT. IN H2O. <br />VOLUME <br />VOL. OF ABS. H2O <br />% SATERATION <br />% SWELL <br />LOAD IN POUNDS <br />DRY STRENGTH <br />WET STRENGTH <br />TSR <br />%VIS. STRIPPING <br />% BROKEN AGG. <br />Tested By: CW <br />Date: 4/27/15 <br />mm.Hg <br />BLOWS <br />CONDITIONED 24 HOURS IN 140 DEGREE F. WATER <br />149.99 <br />95.020 <br />3829.1 <br />2169.5 <br />1659.6 <br />150.01 <br />94.150 <br />3825.9 <br />2175.7 <br />1650.2 <br />74.5 <br />74.1 <br />61.6 <br />63.9 <br />na <br />0.60 <br />0.40 <br />0.50 <br />2179 <br />2272 <br />2226 <br />78.1 <br />78.8 <br />78.4 <br />62.8 <br />66.1 <br />64.4 <br />80.1 <br /><10 <br /><10 <br />84.2 <br />82.1 <br /><10 <br /><10 <br />Reviewed By: AH <br />Date: 4/27/15 <br />G-13 <br />